Oxide phosphor and radiation detector using it, and x-ray ct device

ABSTRACT

An oxide phosphor includes an oxide consisting of at least Gd, Ce, Al, Ga, and O, and has the crystal structure of a garnet structure, the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) of which is more than 0.375 and 0.44 or less, and the atomic ratio Ce/(Ce+Gd) of which is 0.0005 or more and 0.02 or less. This oxide phosphor reduces composition misalignment occurring during sintering, being a drawback of a phosphor having (Gd 1-x Ce x ) 3 Al 5-y Ga y O 12  composition, and has a property of extremely small afterglow and high luminescence efficiency. By using this oxide phosphor as a scintillator of a radiation detector having a light detector, the radiation detector with low afterglow and high output can be obtained. Further, by applying this radiation detector to an X-ray CT apparatus, a tomogram with high resolution and high quality can be obtained.

TECHNICAL FIELD

[0001] The present invention relates to a radiation detector for detecting X-rays, y rays, and the like; and more particularly, the invention relates to an oxide phosphor suitable for a radiation detector such as an X-ray CT apparatus and a positron camera, and to a radiation detector and an X-ray CT apparatus using it.

BACKGROUND OF THE INVENTION

[0002] As a radiation detector for an X-ray CT apparatus there has conventionally been used combinations of a xenon gas chamber, bismuth germanium oxide (BGO single crystal) and a photomultiplier tube, and combinations of a CsI:Tl single crystal or CdWO₄ single crystal and a photodiode. In recent years, a rare-earth phosphor having good radiation-to-light conversion efficiency has been developed, and a radiation detector using a combination of such a phosphor and a photodiode has already been put into practical use.

[0003] A rare-earth phosphor consists of a rare-earth element oxide or a rare-earth element oxysulfide as a base material, to which is added an activator that is a luminescent component. As a rare-earth element oxide phosphor, a phosphor including yttrium oxide and gadolinium oxide as a base material, and a phosphor represented by a formula (Gd_(1-x)Ce_(x))₃Al_(5-y)Ga_(y)O₁₂ have been proposed in Japanese Patent Laid-open Publication JP-A-3-50991 and in International Patent Laid-open Publication WO99/33934 (PCT/JP98/05806), respectively.

[0004] Properties generally required of a scintillator material used in a radiation detector include high luminescence efficiency, short afterglow, and high X-ray stopping power. There are phosphors having high luminescence efficiency among the above-mentioned phosphors, but afterglow time thereof is relatively long. When the afterglow of the scintillator used in X-ray detectors of an X-ray CT apparatus is large, acquired information becomes indistinct along the time-axis. Many conventional scintillator materials have a problem with large afterglow. However, the phosphor (Gd_(1-x)Ce_(x))₃Al_(5-y)Ga_(y)O_(l2) (0.0005≦x≦0.02, 0<y<5), mentioned in the International Patent Laid-open Publication WO99/33934, has excellent scintillator properties including both high light emission output and short afterglow.

[0005] Although it has been confirmed that (Gd_(1-x)Ce_(x))₃Al_(5-y)O_(l2) material in powder form certainly has good scintillator properties, it has been also found that a new problem occurs when manufacturing a scintillator plate using this powder composition. That is, the luminescence efficiency and the afterglow greatly fluctuate when sintering the scintillator plate, and it is hard to obtain stable properties. Especially, it has been revealed that the afterglow properties are significantly deteriorated by sintering and as well the thickness of the sintered body increases. The thick sintered body is indispensable for a low cost manufacturing technique, so that a technique for manufacturing a thick sintered body with low afterglow has been needed.

[0006] An object of the present invention is to provide a phosphor which has a thick plate or block shape suitable for mass production, having high luminescence efficiency to X-rays, extremely low afterglow, and good reproducibility of these properties, by solving the instability of the scintillator properties which is a drawback of the phosphor of (Gd_(1-x)Ce_(x))₃Al_(5-y)O_(l2) composition. Also, another object of the invention is to obtain a radiation detector with large light emission output and low afterglow by using the above phosphor as a scintillator of the radiation detector having a light detector.

[0007] Further, another object of the invention is to provide a tomogram having high resolution and high quality by applying the above radiation detector to an X-ray CT apparatus.

SUMMARY OF THE INVENTION

[0008] To achieve the above-described objects, three-component phosphors (sintered bodies) consisting of (Gd,Ce)—Al—Ga with various compositions were manufactured, and the afterglow thereof was measured. As a result, it was found that scintillator material having low afterglow with significantly greater stability can be obtained, regardless of the plate thickness of the sintered body or the shape and size of the sintered body, when the composition is in a predetermined nonstoichiometric region. Consequently, the invention was completed. That is, the present invention provide an oxide phosphor and a sintered body thereof, described below:

[0009] (1) an oxide consisting at least of Gd, Ce, Al, Ga, and O, the crystal structure of which is a garnet structure, wherein the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) is more than 0.375 and no more than 0.44, and the atomic ratio Ce/(Ce+Gd) is no less than 0.0005 and no more than 0.02.

[0010] (2) an oxide phosphor and a sintered body thereof according to (1), wherein the atomic ratio of Ga/(Al+Ga) is more than 0 and less than 1.0.

[0011] (3) an oxide phosphor and a sintered body thereof according to (1) or (2), having a perovskite structure as an impurity phase.

[0012] (4) an oxide phosphor and a sintered body thereof according to (3), wherein the intensity of the main diffraction line of the perovskite structure in X-ray diffraction measurement is 50% or less of the intensity of the main diffraction line of the garnet structure.

[0013] Further, the present invention provides a radiation detector having a ceramics scintillator and a light detector for detecting light emission of the scintillator, the ceramics scintillator using an oxide phosphor according to (1) to (4).

[0014] Further, the present invention provides an X-ray CT apparatus having an X-ray source; an X-ray detector placed opposite to the X-ray source; a rotating circular plate supporting the X-ray source and the X-ray detector, which is driven to rotate around an object to be examined; and an image reconstructing means for image-reconstructing a tomogram of the object, based on the intensity of X-rays detected by the X-ray detector, wherein the above-described radiation detector is employed as the X-ray detector.

[0015] Hereinafter, the details of the phosphor according to the present invention will be described. The phosphor of this invention is an oxide phosphor including Gd, Al, and Ga as base elements and Ce as the luminescence component, similar to the phosphor (Gd_(1-x)Ce_(x))₃Al_(5-y)O_(l2) (Gd_(1-x)Ce_(x)) (0.0.0005≦x≦0.02, 0<y<5) described in the international publication WO99/33934 of the international patent application by the inventors of the present invention. While the one mentioned in the international publication WO99/33934 is a phosphor having stoichiometric composition, the one according to the present invention has nonstoichiometric composition.

[0016] Incidentally, the description of constituent elements of the phosphor mentioned in the specification of the international publication WO99/33934 constitutes a part of this specification.

[0017]FIG. 3 is a composition diagram of (Gd,Ce)—Al—Ga three-component system. In the drawing, the line designated by reference character S represents the phosphor of the formula (Gd_(1-x)Ce_(x))₃Al_(5-y)O_(l2), described in the international publication WO99/33934, and according to the notation system in this invention it is described by the relations (Gd+Ce)/(Al+Ga+Gd+Ce)=3/8=0.375, 0.0005≦Ce/(Ce+Gd)≦0.02, 0<Ga/(Al+Ga)<1.

[0018] The phosphor according to the invention is the one in the composition region K of nonstoichiometric composition, shown by hatching in FIG. 3.

[0019] Concretely, the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) is more than 0.375 and no more than 0.44, and the atomic ratio of Ce/(Ce+Gd) is no less than 0.0005 and no more than 0.02.

[0020] If the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) is 0.375 or less, among the scintillator properties the afterglow particularly increases by hundredfold, and the light emission output decreases by 30% or more. On the other hand, if the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) is above 0.44, the damping factor of afterglow 300 ms after stopping the excitation source is a stably low value, about 4×10⁻⁵. However, the Gd(Ga,Al)O₃-phase of the perovskite structure constituting a hetero phase is generated, comprising 50% or more of the host crystal of the garnet structure. Further, the light emission output is deteriorated by 40%.

[0021] If Ce/(Ce+Gd) is outside the above range, sufficient light emission cannot be obtained. The atomic ratio Ga/(Al+Ga) is preferably more than 0 and less than 1.0. If this atomic ratio is out of the above range, sufficient emission intensity cannot be obtained, even if Ce is doped.

[0022] The above change of the scintillator properties caused by variation of atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) can be understood from the following consideration of the crystal structure.

[0023]FIG. 4 shows the garnet structure having theoretical stoichiometric composition represented by (Gd_(1-x)Ce_(x))₃Al_(5-y)O_(l2). The ion radii of Gd and Ce are 0.97 Å and 1.07A respectively, and those of Al and Ga are 0.51 Å and 0.62 A respectively. Now, consider the case of nonstoichiometric composition, the composition of which is shifted from the stoichiometric composition (Gd,Ce):(Al,Ga)=3:5. When Gd components exceed the stoichiometric composition, the Gd ions cannot be substituted into the (Al,Ga) sites since the ion radius of the Gd ion is large. These extra Gd ions thus are present in the garnet structure host crystal, the hetero phase of which is the GdAlO₃ perovskite structure.

[0024] On the other hand, when the Gd component is less than that of the stoichiometric composition, that is, when the (Al, Ga) components exceed the stoichiometric composition range, Al or Ga ions having small radius can be substituted into the Gd sites and take on the garnet structure.

[0025] From this consideration of the crystal structure, property change of light emission output and afterglow can be described as follows: When there is an excess of Gd component, a hetero phase (absorber) which does not emit light is generated in the host crystal along with increase of the Gd components and the light emission output is gently reduced. However, since the hetero phase GdAlO₃ is not involved with light emission, it hardly at all affects the afterglow properties. On the other hand, when there is less of the Gd component than in the stoichiometric composition, the crystal structure retains the garnet structure. However, the Al or Gs ion deforms the structure of the crystal energy band and generates energy levels which allow electron transition to a forbidden band, since the Al or Gs ions which substitute for Gd sites are impurity ions in the garnet structure. It appears that as a consequence the afterglow becomes large, and light emission output is also deteriorated since efficiency of energy transmission from the host crystal to main luminescence center Ce³⁺ deteriorates.

[0026] In this manner, in a phosphor including Ce as a luminescence element and a host crystal having a garnet structure including at least Gd, Al, Ga, and O, luminescence properties and afterglow properties are greatly deteriorated even when the composition is slightly changed to have less (Gd+Ce) than in the stoichiometric composition (Gd+Ce)/(Al+Ga+Gd+Ce)=0.375.

[0027] Theoretically, good scintillator properties should be obtained when the stoichiometric composition (Gd+Ce)/(Al+Ga+Gd+Ce)=0.375. However, in the process of manufacturing a scintillator plate, sintering easily causes the (Gd+Ce) components in this phosphor to decrease. Particularly, such influence becomes significant when a thick sintered body is employed. When phosphor powder of the stoichiometric composition is employed, phosphor properties of the sintered body are deteriorated. Therefore, in the present invention, the (Gd+Ce) component of the phosphor powder composition is made excessive by the amount whereby good scintillator properties can be obtained, compensating for the composition misalignment effect by sintering. Thus, a phosphor element with low afterglow can be manufactured even when a thick sintered body is employed.

[0028] The crystal form of the phosphor according to this invention is not particularly limited, and either a single crystal a poly crystal can be employed. However, the poly crystal is preferable in terms of ease of manufacture and uniformity of properties. The poly crystal can be obtained by 1) the process of synthesizing the powder which is to be a raw material of the scintillator, and then 2) the process of sintering the powder. To obtain an oxide of the desired garnet structure, smaller crystal-grain diameter of the synthesized powder is preferable, 1.0 μm or less being desirable.

[0029] The methods of powder synthesis include 1) a method basically using a conventional oxide-mixing method, 2) a method using a liquid phase, such as a coprecipitation method and a sol-gel method, 3) a method based on the oxide-mixing method, in which the synthesized powder is finely divided by mechanical means, and the like.

[0030] When using the conventional oxide-mixing method, the following manufacturing processes are feasible. A predetermined amount of powder including such constituent metallic material as Gd₂O₃, Ce₂O₃, Ga₂O₃ in powder form is weighed, and the powder is mixed in wet process using a ball mill, an automatic mortar, or the like. This mixed powder is sintered in 1000° C.˜1700° C. air or oxygen for several hours, thus resulting in the synthesized powder for a scintillator. If necessary, generation of a Gd—Ce—Al—Ga—O-system garnet structure can be improved by using as flux a potassium compound such as K₂S0 ₄ or a fluorine compound such as BaF₂.

[0031] In the process using coprecipitation, synthesis can be done as follows, for example: A predetermined amount of gadolinium nitrate, alumina nitrate, gallium nitrate, and cerium nitrate is weighed so as to make a compound nitrate water solution, and urea is made to coexist with nitrate ion, urea concentration being fifteen times as much as the total metal-ion concentration. This water solution is heated to 70-100° C. to hydrolyze the urea, and Gd-Al-Ga-O precursor is deposited.

[0032] The deposition is repeatedly cleaned so as to lower the concentration of negative ions, being useless, in the deposition to less than 1000 ppm, and is dried at about 120° C. and subject to temporary sintering at about 1200° C., whereby the scintillator powder is made. The drying temperature should be 90° C. or more for good evaporation of moisture, and the temporary-sintering temperature should be 900° C. or more, temperatures at which the garnet structure is generated. Heat treatment in which crystal grains of the generated garnet structure are developed must be avoided.

[0033] The material used in the coprecipitation method is not limited to nitrate, and nitrate, sulfate, oxalate and the like of any kind of metal may be employed. Depending on the circumstances, several kinds of metallic salts may be mixed and used. Ammonium bicarbonate may also be used instead of urea.

[0034] The Gd—Ce—Al—Ga—O precursor can also be deposited by adding to the compound metallic solution 1) urea and ammonium lactate, 2) ammonium bicarbonate and ammonia water, 3) ammonium sulfate and ammonia water, or 4) oxygenated water as a masking agent and ammonium sulfate and ammonia water.

[0035] Finely dividing powder in mechanical manner is also a method suitable for obtaining the garnet structure by sintering. That is, as in the above oxide-mixing method, a predetermined amount of oxide of the metal to be a component of the composition is weighed and is mixed by an automatic mortar about thirty minutes. The mixed powder is subject to temporary sintering at around 1500° C., and is mechanically grinded. A grinding method with high grinding energy, such as a ball mill or preferably a planetary ball mill, should be employed. Thus, powder having 0.01 to 0.5 μm grain diameter can be easily obtained.

[0036] Sintering of thus-synthesized powder can be done using a hot pressing method, an HIP method, a pressureless sintering method, simultaneous use of the pressureless sintering method and the HIP method, and the like. In any case, relative concentration of the sintered body should be 99.0% or more, and preferably 99.5% or more. “Relative concentration” is a percentage of the actual concentration, theoretical concentration of the material being 100. If the relative concentration becomes low, scattering of light increases and light transmission is extremely deteriorated, whereby sufficient light output cannot be obtained. Therefore, the relative concentration should be within the above range.

[0037] When the hot pressing method is employed, the above-described synthesized powder is shaped with a mold with 500 kgf/cm² pressure, set into hot-press mold, and is sintered under about 500 kgf/cm² pressure in vacuum, air, or oxygen at sintering temperature 1000° C.-1700° C. In this manner, the phosphor having 99.5% or more relative concentration can be easily obtained.

[0038] In the HIP method, the synthesized powder is put into a metallic capsule made from iron, W, Mo, or the like, vacuum sealed, and sintered at about 1400° C. under 2000 atm pressure.

[0039] In the pressureless sintering method, the synthesized powder is shaped with a mold under about 500 kgf/cm² pressure, and is then subject to cold isostatic pressing (CIP) with about 3000 kgf/cm² pressure, and is sintered several to several-ten hours at about 1400-1800° C. When the temperature is over 1800° C., the sample melts. When the temperature is under 1400° C., the sintering concentration becomes about 90% and sufficient sintering concentration cannot be obtained.

[0040] To obtain a sintered body with 99.5% or more relative concentration by the pressureless sintering method, 1) powder to which a sintering auxiliary agent is added, or 2) minute powder of sub-micron size, is preferably employed as the synthesized powder. Also, since pores are closed by pressureless sintering when the relative concentration of the sintered body is about 93.0% or more, the phosphor having 99.5% or more relative concentration can be easily obtained by adding the capsule-free HIP method in which a metallic capsule is not needed.

[0041] In the phosphor obtained by the above-described method according to the present invention, the host crystal has the garnet structure, the material has its main luminescence spectrum peak at about 535 nm, and the damping factor of afterglow 300 ms after stopping the excitation source is 0×10⁻⁴ or less. This oxide phosphor has high light emission output and extremely small afterglow, whereby it is suitable for use as a radiation detector of X-rays and the like, particularly for a radiation detector for X-ray CT apparatus and a positron camera.

[0042] As a light detector of the radiation detector according to the present invention, a PIN-type diode is employed. This photodiode has high sensitivity, fast response time, and wavelength sensitivity through the visible ray area and the near infrared ray area, whereby the phosphor according to the present invention well matches the luminescence wavelength.

[0043] Further, in the X-ray CT apparatus according to the present invention, the above-described radiation detector is employed as an X-ray detector. By employing such an X-ray detector, X-rays can be detected with high detecting efficiency, whereby the sensitivity thereof is greatly improved in comparison with an X-ray CT apparatus using a conventional scintillator (CdWO₄, for example). Further, since the afterglow is extremely low, an image having high image-quality and high resolution can be obtained.

BRIEF DESCRIPTION OF THE DRAWINGS

[0044]FIG. 1 is a schematic view showing a radiation detector (X-ray detector) using a scintillator according to the present invention;

[0045]FIG. 2 is a schematic view showing the structure of an X-ray CT apparatus in one embodiment according to the present invention;

[0046]FIG. 3 is a diagram showing (Gd+Ce)—Al—Ga three-component-system composition in an oxide phosphor according to the invention;

[0047]FIG. 4 is a diagram showing the garnet crystal structure of an oxide phosphor according to the present invention; and

[0048]FIG. 5 is a diagram showing dependency of luminescence properties of the oxide phosphor upon composition according to the present invention.

BEST MODE FOR CARRYING OUT THE INVENTION

[0049] An embodiment of an X-ray detector and an X-ray CT apparatus according to the present invention will be described with reference to the drawings.

[0050]FIG. 1 shows one example of an X-ray detector 10 using scintillators according to the invention. In the X-ray detector 10, a scintillator 11 is adhered to a photodiode 12, and it is covered with a covering member 12 for preventing light emitted by the scintillators from leaking outside. X-rays pass through the covering member, which is made of aluminum or another material that reflects light.

[0051] Incidentally, when applying the X-ray detector according to the invention to an X-ray CT apparatus, this X-ray detector is constructed such that several hundreds to several ten thousands of elements (detection channels) are arranged. FIG. 1 only shows three detection elements which are one part of this.

[0052] In this X-ray detector, the scintillator 111 includes a phosphor according to the invention, which has extremely small afterglow and high light emission output in comparison with a conventional scintillator. Since the scintillator 11 has its luminescence peak near 535 nm wavelength, which is relatively close to the sensitivity wavelength of Si photodiodes, X-rays absorbed by the scintillator 11 are photoelectrically converted by the photodiodes with high efficiency. Therefore, the X-ray detector according to the invention has excellent performance, including high sensitivity and extremely small afterglow.

[0053]FIG. 2 shows outline of an X-ray CT apparatus according to the invention. This apparatus includes a gantry portion 18, an image reconstruction unit 22, and a monitor 23. The gantry portion 18 is provided with a rotating circular plate 19 having an opening 20 into which an object to be examined is inserted, an X-ray tube 16 mounted on this rotating circular plate, a collimator 17 which is mounted on the X-ray tube and controls the direction of X-ray irradiation, an X-ray detector 15 which is mounted on the rotating circular plate opposite to the X-ray tube, a detector circuit 21 for converting X-ray dose detected by the X-ray detector 15 into a particular electric signal, and a scanning control circuit 24 for controlling rotation of the rotating circular plate and width of X-ray irradiation.

[0054] The X-ray detector 15 is constructed such that a number of detection elements, each of which combines the scintillator 11 and the photodiode 13 according to the invention, shown in FIG. 1, are lined up along the circumference of the rotating circular plate 19. This X-ray detector 15 detects the dose of X-rays which are radiated and pass through the object.

[0055] The image reconstruction unit 22 includes an input device 25 for inputting the object's name, examination date, examination conditions, and the like, an image calculating circuit (not shown) for performing data-processing on measured data sent from the detector circuit 21, an image information addition unit (not shown) for adding information such as the object's name, the examination date, and the examination conditions which was input by the input device 25, to CT images created by the image calculation circuit, and a display circuit (not shown) for adjusting display gain of the CT images to which image information is added and output to the monitor 23.

[0056] In the X-ray CT apparatus having such a structure, X-rays are irradiated from the X-ray tube 16 to the object which is laid on a bed (not shown) provided in the opening 20. The X-rays are provided with directivity by the collimator 17, and they are detected by the X-ray detector 15. By rotating the rotating circular plate 19 around the object, X-rays are detected while changing the radiating direction of X-rays, tomograms are created by the image reconstruction unit 22, and they are displayed on the monitor 23.

[0057] Here, as the X-ray detector 15 a detector using the phosphor according to the invention, which has low afterglow and large emission intensity, is employed. Therefore, the image is not deteriorated due to afterglow, and images having high image quality and high resolution can be obtained.

[0058] Embodiments

[0059] Hereinafter, the embodiments of the present invention will be described in detail.

[0060] [Embodiment 1]

[0061] Gd₂O₃, Ce₂(C₂O₄)₃, Al₂O₃, and Ga₂O₃ were used as material powder. The atomic ratio Ce/(Ce+Gd) and Ga/(Al+Ga) were fixed at 0.004 and 0.44, respectively. The material powder was weighed out so that (Gd+Ce)/(Al+Ga+Gd+Ce) was 0.325 to 0.45, which corresponds to varying the composition along the thick line L in the composition diagram of FIG. 3.

[0062] Next, the measured material powder, alumina balls, and ion exchange water were put into a vessel made of polyethylene, and they were mixed by a ball mill for twelve hours. This mixed powder was put into an evaporating dish and is dried, and the dried powder was sized by a nylon sieve. An alumina crucible was filled with the sized powder, and it was sintered in 1500° C. oxygen for four hours.

[0063] X-rays were irradiated from an X-ray source (120 kV, 0.5 mA) to the synthesized powder, and the afterglow and the luminescence intensity were measured. In this measurement, a detector using photodiodes is located 15 cm from the X-ray source and the amount of light was measured. The afterglow is measured in terms of the damping factor 300 ms after stopping the X-rays, and the emission intensity is represented by a relative value.

[0064] The amount of generated hetero-phase is calculated from powder X-ray diffraction tests. The hetero-phase amount is defined as the ratio between the strength of the main diffraction line of the garnet crystal structure which is the matrix and the strength of the main diffraction line of the perovskite crystal structure, which is the hetero-phase.

[0065]FIG. 5 shows the result thereof. As is clear from the figure, the hetero-phase GdAlO₃ is generated in proportion to the amount of composition misalignment from the stoichiometric composition when the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) is larger than 0.375. Afterglow properties are hardly changed at all, stable at about 4×10⁻⁵, which is an extremely good value, as the atomic ratio is raised to 0.44. On the other hand, luminescence properties are moderately deteriorated with increase of (Gd+Ce) component.

[0066] When the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) exceeds 0.44, light emission output becomes about 60% of the stoichiometric composition or less, and the ratio of the perovskite phase, which is the hetero-phase present in the phosphor, is over 50%, indicating that the synthesized powder having such an atomic ratio is not suitable as phosphor material. On the other hand, when (Gd+Ce) component is less than that in the stoichiometric composition, afterglow properties and luminescence properties are greatly deteriorated in response to slight composition misalignment. Even when the (Gd+Ce)/(Al+Ga+Gd+Ce) composition is reduced by only 0.003 in comparison with the stoichiometric composition, the value of afterglow becomes about hundredfold, and light emission output is decreased by about 30%. Although the (Gd+Ce) component is decreased, the crystal structure remains the garnet structure, and only when (Gd+Ce)/(Al+Ga+Gd+Ce) is 0.325 the hetero-phase is finally generated.

[0067] [Embodiments 2 and 3]

[0068] Gd₂O₃, Ce₂(C₂O₄)₃, Al₂O₃, and Ga₂O₃ were used as material powder. The atomic ratio Ce/(Ce+Gd) and Ga/(Al+Ga) were fixed as 0.004 and 0.44, respectively. In this manner, a nonstoichiometric composition sample with (Gd+Ce)/(Al+Ga+Gd+Ce)=0.380 was manufactured. The material powder was measured out according to the composition in Chart 1.

[0069] Next, the measured material powder, alumina balls, and ion exchange water were put into a vessel made of polyethylene, and they were mixed by a ball mill for about 12 hours. The mixed powder was put into an evaporating dish and is dried. The dried powder was sized by a nylon sieve. An alumina crucible was filled with the sized powder, and is sintered in 1500° C. oxygen for about four hours. This synthesized powder was molded using a mold having 160 mm inner diameter with 500 kgf/cm² pressure, and a molded body was thus made. It was then set in a hot press die and hot-press sintered in vacuum at 1475° C. for four hours under 500 kgf/cm² pressure, and sintered bodies having 4.7 mm (Embodiment 2) thickness and having 15 mm (Embodiment 3) thickness were thus obtained. Relative concentrations of these sintered bodies were both 99.9% or more.

[0070] The sintered bodies that were obtained by the above method were sliced in the plate-thickness direction, one (Embodiment 2) or five (Embodiment 3) wafers having 160 mm inner diameter are cut out, the wafers were cut into a predetermined length and machined so as to have 108 mm width, and thus, scintillator plates were manufactured. These scintillator plates were annealed in oxygen for four hours, and afterglow and emission intensity were then measured. The result thereof is shown in the chart 1.

[0071] Incidentally, the measurement of afterglow and emission intensity is performed for detectors made by combining the above-manufactured scintillator plates and photodiodes, and the detector is located 110 cm away from the X-ray source (120 kV, 150 mA). Afterglow is measured in terms of the damping factor 300 ms after stopping the X-rays, and emission intensity is represented by a relative value with the emission intensity of CdWO₄ set as 1.

COMPARATIVE EXAMPLES 1 To 3

[0072] Sintered bodies respectively having 4.7 mm width, 10.0 mm width, and 15.0 mm width were manufactured in the same manner as those in Embodiments 2 and 3, except that the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) of the starting material powder is 0.375. One, three and five wafers having 160 mm inner diameter were cut out respectively from the above-obtained sintered bodies, and scintillator plates (Comparative Examples 1 to 3) were thus produced. These scintillator plates were also annealed in the same manner as Embodiments 0.2 and 3, and afterglow and emission intensity were measured. The result thereof is shown in the chart 1.

[0073] Incidentally, in the interior of the respective scintillators, great difference of afterglow and emission intensity was not found between in the plate-thickness direction and in the diameter direction. CHART 1 Sintered Emission Body (Gd + Ce)/ Intensity Thickness (Gd + Ce + Afterglow (versus (mm) Al + Ga) Gd Ce Al Ga (300 ms) CsWO₄) Embodiment 2 4.7 0.380 3.03 0.01 2.78 2.18 1.2 × 10⁻⁵ 2.3 Embodiment 3 15.0 0.380 3.03 0.01 2.78 2.18 1.4 × 10⁻⁵ 2.3 Comp. Ex. 1 4.7 0.375 2.99 0.01 2.80 2.20 2.0 × 10⁻⁵ 2.2 Comp. Ex. 2 10.0 0.375 2.99 0.01 2.80 2.20 3.0 × 10⁻⁴ 2.0 Comp. Ex. 3 15.0 0.375 2.99 0.01 2.80 2.20 9.50 × 10⁻⁴  1.7

[0074] In the samples of the stoichiometric composition (Comparative Examples 1 to 3), afterglow was drastically increased as the plate thickness was increased. When the plate thickness was 15 mm, the value of the afterglow was increased by double digits. The emission intensity was also deteriorated. On the other hand, in the samples of nonstoichiometric composition (Embodiment 2 and 3), the afterglow was not increased and the emission intensity also was not deteriorated even when the plate thickness was increased from 4.7 mm to 15 mm. Incidentally, the difference between 0.375 and 0.38 in the atomic ratios of (Gd+Ce)/(Al+Ga+Gd+Ce), being the measured out compositions, is not generated by a mere measuring error in manufacturing the material or an error occurring when the material powder absorbs moisture. This is because such errors are kept within 0.001 at the maximum.

EMBODIMENTS 4 TO 13, AND COMPARATIVE EXAMPLES 4 to 11

[0075] Sintered bodies were manufactured in the same manner as those in Embodiments 2 and 3, except that the atomic ratio of Gd, Ce, Al, and Ga was made as shown in Chart 2. Though the atomic ratio Ga/(Al+Ga) is 0.44 in the Comparative Examples 1 to 3 and Embodiments 2 and 3, that in the Comparative Examples 4 to 7 and in Embodiments 4 to 8 is 0.70, and that in the Comparative Examples 8 to 11 and in Embodiments 9 to 13 is 0.30. Ce concentration is fixed so that the atomic ratio Ce/(Ce+Gd) is 0.004, and the ratio (Gd+Ce)/(Al+Gd+Gd+Ce) is varied. The thickness of all sintered bodies is 15 mm.

[0076] The obtained sintered bodies are sliced in the plate-thickness direction. After cutting, the sintered bodies are machined into plates with thickness of 1.8 mm, and are annealed at 1300° C.

[0077] The hetero-phase amount in these scintillator plates was measured as the intensity ratio between the main peak of the diffraction line of the garnet structure and that of the hetero phase, which are obtained by an X-ray diffraction apparatus. Detectors are made by combining the obtained scintillator plates and photodiodes, they are located 110 cm from an X-ray source (120 kV, 1.50 mA), as in Embodiments 2 and 3, and the emission intensity and the afterglow were thus measured. The emission intensity was represented by a relative value with the value of CdWO₄ set to be 1, and the afterglow measured in terms of the damping factor 300 ms after stopping the X-rays. The result thereof is shown in Chart 2 and Chart 3. CHART 2 Hetero- Emission (Gd + Ce)/ phase Intensity (Gd + Ce + amount Afterglow (versus Al + Ga) Gd Ce Al Ga (%) (300 ms) CdWO₄) Comp. Ex. 4 0.35 2.79 0.01 1.56 3.64 0 1.5 × 10⁻³ 1.3 Comp. Ex. 5 0.37 2.95 0.01 1.51 3.53 0 1.5 × 10⁻³ 1.3 Comp. Ex. 6 0.375 2.99 0.01 1.50 3.50 0 1.9 × 10⁻⁴ 1.8 Embodiment 4 0.376 3.00 0.01 1.50 3.49 0 1.0 × 10⁻⁵ 1.9 Embodiment 5 0.378 3.01 0.01 1.49 3.48 0 1.0 × 10⁻⁵ 1.9 Embodiment 6 0.39 3.11 0.01 1.46 3.42 9 1.0 × 10⁻⁵ 1.8 Embodiment 7 0.41 3.27 0.01 1.42 3.30 24 1.5 × 10⁻⁵ 1.6 Embodiment 8 0.44 3.51 0.01 1.34 3.14 39 2.5 × 10⁻⁵ 1.5 Comp. Ex. 7 0.46 3.67 0.01 1.30 3.02 58 3.5 × 10⁻⁵ 1.2

[0078] CHART 3 Emission (Gd + Ce)/ Hetero- Intensity (Gd + Ce + Phase Afterglow (versus Al + Ga) Gd Ce Al Ga Amount (300 ms) CdWO₄) Comp. Ex. 8 0.35 2.79 0.01 3.64 1.56 0 1.5 × 10⁻³ 1.1 Comp. Ex. 9 0.37 2.95 0.01 3.53 1.51 0 1.5 × 10⁻³ 1.2 Comp. Ex. 10 0.375 2.99 0.01 3.50 1.50 0 9.8 × 10⁻⁵ 1.6 Embodiment 9 0.376 3.00 0.01 3.49 1.50 0 1.0 × 10⁻⁵ 1.7 Embodiment 10 0.378 3.01 0.01 3.48 1.49 0 1.0 × 10⁻⁵ 1.7 Embodiment 11 0.39 3.11 0.01 3.42 1.46 8 1.0 × 10⁻⁵ 1.6 Embodiment 12 0.41 3.27 0.01 3.30 1.42 29 2.0 × 10⁻⁵ 1.4 Embodiment 13 0.44 3.51 0.01 3.14 1.34 40 3.5 × 10⁻⁵ 1.3 Comp. Ex. 11 0.46 3.67 0.01 3.02 1.30 58 3.8 × 10⁻⁵ 1.1

[0079] Even when the atomic ratio Ga/(Al+Ga) is 0.70 or 0.30, the hetero-phase amount is small and the emission intensity is relatively large as long as the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) is 0.375 or less (Comparative Examples 4 to 6, 8 to 10). However, since thus obtained material had a damping factor of 10-3 to 10-4 of the afterglow after 300 ms, it was shown that the sintered body used therein became large and was not suitable as scintillator material. When the atomic ratio (Gd+Ce)/(Al+Ga+Gd+Ce) was over 0.44 (Comparative Example 7 and 11), the hetero-phase amount was over 50%, and the emission intensity also was lowered.

[0080] On the other hand, the scintillators according to Embodiments 4 to 13 of the present invention have extremely short afterglow and high emission intensity, whereby it is understood that they have excellent scintillator properties.

EMBODIMENTS 14 TO 17 AND COMPARATIVE EXAMPLES 12 AND 13

[0081] Sintered bodies (15 mm thickness) of Embodiments 14 to 17 and of the Comparative Examples 12 and 13 were manufactured in the same manner as those in Embodiments 2 and 3, except that the atomic ratio (Ge+Ce)/(Al+Ga+Gd+Ce) was set to be 0.38, the atomic ratio Ce/(Ce+Gd) as Ce concentration was set to be 0.004, and the atomic ratio Ga/(Al+Ga) was varied from 0.0 to 1.0.

[0082] These sintered bodies were sliced in the plate-thickness direction. After cutting, they were machined so as to make their thickness 1.8 mm. Scintillator plates were thus made, and they were annealed at 1300° C.

[0083] Detectors are made by combining the obtained scintillator plates and photodiodes, they are located 110 cm from an X-ray source (120 kV, 150 mA), and the afterglow and the emission intensity are thus measured. The afterglow is measured in terms of the damping factor 300 ms after stopping X-rays, and the emission intensity is represented by a relative value with respect to the value 1 of CdO4. The results thereof are shown in Chart 4. CHART 4 Emission (Gd + Ce)/ Intensity (Gd + Ce + Ga/ Afterglow (versus Al + Ga) (Al + Ga) Gd Ce Al Ga (300 ms) CdWO₄) Comp. Ex. 12 0.38 0.00 3.03 0.01 4.96 0.00 — 0.0 Embodiment 14 0.38 0.05 3.03 0.01 4.71 0.25 2.0 × 10⁻⁵ 1.2 Embodiment 15 0.38 0.30 3.03 0.01 3.47 1.49 1.5 × 10⁻⁵ 2.1 Embodiment 16 0.38 0.60 3.03 0.01 1.98 2.98 2.0 × 10⁻⁵ 2.0 Embodiment 17 0.38 0.90 3.03 0.01 0.50 4.46 1.5 × 10⁻⁵ 1.3 Comp. Ex. 13 0.38 1.00 3.03 0.01 0.00 4.96 — 0.0

[0084] From the chart, it is found that, although the scintillators of Embodiments 14 to 17 have excellent afterglow and emission intensity properties, the emission intensity of the scintillators whose atomic ratio Ga/(Al+Ga) are 0 or 1.0 (Comparative Example 12 and Comparative Example 13), much lower, and the sintered bodies thereof are not suitable for use as a scintillator.

EMBODIMENTS 18 TO 21 AND COMPARATIVE EXAMPLES 14 AND 15

[0085] The scintillators of Embodiments 14 and 15 were manufactured in the same manner as those of Embodiments 2 and 3, except that the atomic ratio Ce/(Ce+Gd) is varied from 0.002 to 0.04. Incidentally, the atomic ratios (Gd+Ce)/(Al+Ga+Gd+Ce) and Ga/(Al+Ga) are fixed respectively to 0.38 and 0.44. The thickness of the sintered bodies is 15 mm. The result thereof is shown in Chart 5. CHART 5 Emission (Gd + Ce)/ Intensity (Gd + Ce + Ce/ Afterglow (versus Al + Ga) (Ce + Gd) Gd Ce Al Ga (300 ms) (CdWO₄) Comp. Ex. 14 0.38 0.0002 3.04 0.0006 2.78 2.18 3.5 × 10⁻⁴ 0.8 Embodiment 18 0.38 0.0005 3.04 0.0015 2.78 2.18 4.8 × 10⁻⁵ 1.6 Embodiment 19 0.38 0.001 3.04 0.0030 2.78 2.18 1.5 × 10⁻⁵ 2.1 Embodiment 20 0.38 0.005 3.02 0.0152 2.78 2.18 1.0 × 10⁻⁵ 2.0 Embodiment 21 0.38 0.02 2.98 0.0608 2.78 2.18 3.0 × 10⁻⁵ 1.5 Comp. Ex. 15 0.38 0.04 2.92 0.1216 2.78 2.18 2.5 × 10⁻⁵ 0.5

[0086] From the chart, it is found that, the scintillators of Embodiments 18 to 21 have excellent properties of afterglow and emission intensity, and the scintillators of the Comparative Examples 14 and 15, where the atomic ratio Ce/(Ce+Gd) is respectively less than 0.0005 and more than 0.02 are not suitable as the required scintillator became the emission intensities thereof are extremely low.

INDUSTRIAL AVAILABILITY

[0087] According to the present invention, a phosphor having extremely low afterglow and high luminescence efficiency can be provided by reducing the composition misalignment occurring during sintering, which is a drawback of a phosphor of (Gd_(1-x)Ce_(x))₃Al_(5-y)Ga_(y)O₁₂ composition. Further, by using this phosphor as a scintillator for a radiation detector having a light detector, a radiation detector having low afterglow and high output can be obtained. By applying this radiation detector to an X-ray CT apparatus, a tomogram having high resolution and high quality can be obtained. 

1. An oxide phosphor having the oxide consisting of at least Gd, Ce, Al, Ga, and O, wherein a crystal structure of said oxide is a garnet structure, and the atomic ratio Ce/(Ce+Gd) is no less than 0.0005 and no more than 0.02.
 2. An oxide phosphor according to claim 1, wherein the atomic ratio Ga/(Al+Ga) is more than 0 and less than 1.0.
 3. An oxide phosphor according to claim 1 or 2, further including an impurity phase of a perovskite structure.
 4. An oxide phosphor according to claim 3, wherein the intensity of a main diffraction line of the perovskite structure in an X-ray diffraction measurement is 50% or less with respect to the intensity of the main diffraction line of the garnet structure.
 5. An oxide phosphor according to claims 1 to 4, wherein oxide powder is synthesized by at least one of the following methods: an oxide-mixing method, a coprecipitation method, and a mechanically grinding method using material powder.
 6. An oxide phosphor according to claim 5, wherein the diameters of crystal grain of the oxide-synthesized powder are 1 μm or less.
 7. An oxide phosphor according to claim 5, wherein said oxide-synthesized powder is sintered by at least one of the following methods: a hot-press method, an HIP method, a pressureless sintering method, and simultaneous use of a pressureless sintering method and an HIP method.
 8. An oxide phosphor according to claim 7, wherein the relative concentration of the sintered body of the oxide-synthesized powder is 99.0% or more.
 9. A scintillator including a sintered body of the oxide phosphor according to any of claims 1 to
 4. 10. A radiation detector in an X-ray detector including a ceramics scintillator and a light detector for detecting light emission of said scintillator, wherein the scintillator according to claim 9 is employed as said ceramics scintillator.
 11. An X-ray CT apparatus comprising: an X-ray source; an X-ray detector located opposite to said X-ray source; a rotating disk holding said X-ray source and said X-ray detector, which is driven to rotate around an object to be examined; and an image reconstruction means for image-reconstructing a tomogram of said object on the basis of intensity of X-rays detected by said X-ray detector, wherein a radiation detector according to claim 10 is employed as said X-ray detector. 